Low Carbon Steel Hot-rolled Sheet Steel ASTM A36 Thickness 75mm 60mm 15mm
- China
- 15-25 Working Days
- Factory Direct Supply
Hot Rolled Steel A36 (ASTM A36) is the most commonly available grades of the hot-rolled steels which has good overall mechanical properties, is easily fabricated and may be formed hot or cold. Due to the hot roll process the surface on this steel will be rough when compared to cold rolled. ASTM A36 yield strength is also less than C1018.
E-mail：
admin@jinshugc.com
WhatsApp：
8615315750155
ASTM A36 Low Carbon Steel Hot-rolled Sheet Steel
Hot Rolled Steel A36 (ASTM A36) is the most commonly available grades of the hot-rolled steels which has good overall mechanical properties, is easily fabricated and may be formed hot or cold. Due to the hot roll process the surface on this steel will be rough when compared to cold rolled. ASTM A36 yield strength is also less than C1018.
A36 Hot Rolled Steel Plate Description
A36 hot rolled steel plates are an excellent candidate for most processing techniques. A36 hot rolled steel plates have a rough, blue-grey finish, dull rounded edges and have inexact dimensions throughout length. A36 material is a low carbon steel, often referred to as mild steel which is long lasting and durable. Common applications include base plates, brackets, gussets and trailer fabrication. ASTM A36 / A36M-08 is the standard specification for carbon structural steel.
Product Parameters
Product Name | A36 Hot Rolled Steel Plate |
Production Process | Hot Rolling |
Material Standards | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, etc. |
Width | 100mm-3000mm |
Length | 1m-12m, or Customized Size |
Thickness | 0.1mm-400mm |
Delivery Conditions | Rolling, Annealing, Quenching, Tempered or Standard |
Surface Process | Ordinary, Wire Drawing, Laminated Film |
Chemical Composition
| Element | Percentage |
| C | 0.26 |
| Cu | 0.2 |
| Fe | 99 |
| Mn | 0.75 |
| P | 0.04 max |
| S | 0.05 max |
Mechanical Properties
| Imperial | Metric | |
| Density | 0.282 lb/in3 | 7.8 g/cc |
| Ultimate Tensile Strength | 58,000 psi | 400 MPa |
| Yield Tensile Strength | 47,700 psi | 315 MPa |
| Shear Strength | 43,500 psi | 300 MPa |
| Melting Point | 2,590 - 2,670 °F | 1,420 - 1,460 °C |
Scope of Application
● Trailers
● Walkways
● Ramps
● Structural supports
● General fabrication